Tabular Corundum Fused Alumina 99% Alumina Tabular Thermal Refractory Tabular Alumina mo le Glass Furnace Fa'atau Atoa
Aoao atili- Tulaga o le Oloa:Pauta Pa'epa'e
- Fa'amatalaga:0-1mm 1-3mm 3-5mm 5-8mm 325#
- Kalave e Vaaia:3.5g/cm3 minute
- Porosity e foliga mai:5.0% maualuga
- Fa'asusuina o le Vai:1.5% maualuga
- Al2O3:99.2 minute
- Na2O :0.40 maualuga
- Fe2O3:0.10 maualuga
- Fe2O3:0.10 maualuga
-
Tabular Alumina mo le Refractory Dry Ramming Mass Sintered Tabular Alumina mo Mea Mata Refractory
Aoao atili- Tulaga o le Oloa:Pauta Pa'epa'e
- Fa'amatalaga:0-1mm 1-3mm 3-5mm 5-8mm 325#
- Kalave e Vaaia:3.5g/cm3 minute
- Porosity e foliga mai:5.0% maualuga
- Fa'asusuina o le Vai:1.5% maualuga
- Al2O3:99.2 minute
- Na2O :0.40 maualuga
- Fe2O3:0.10 maualuga
- Fe2O3:0.10 maualuga
-
1mm 2mm 3mm Zirconia Beads Zirconium Oxide Grinding Balls Industrial Ceramic
Aoao atili- Mafiafia:>3.2g/cm3
- Mafiafia o le Tele:>2.0g/cm3
- Ma'a'a o Moh:≥9
- Tele:0.1-60mm
- Mataupu:95%
- Foliga:Polo
- Fa'aaogāga:Ala o mea olo
- Fa'a'olo'olo:2ppm%
- Lanu:Lanu pa'epa'e
-
B40 B60 B80 B100 Oneone Seramika Mama 95% Zirconia Zro2
Aoao atili- Foliga:Lapotopoto
- Mamafa Fa'apitoa:4.3G/Cm3
- Mafiafia o le Tele:2.1-2.3G/Cm3
- Tele:B20-B1000
- Faigata: 7
- Meafaitino:Zr2o
- Ma'a'a o Vicker:700HV
- Fa'ata'amilosaga:≥80%
- Lanu:Samasama-Pa'epa'e
-
Efuefu Sili Ona Lelei o le Zirconia Dioxide Zro2 Zirconium Oxide
Aoao atili- Tele o le vaega:20nm, 30-50nm, 80-100nm, 200-400nm, 1.5-150um
- Mafiafia:5.85 G/Cm³
- Tulaga e Liusuavai ai:2700°c
- Pupula:4300 ºC
- Mataupu:99%-99.99%
- Talosaga:Oloa Seramika, Maa, Oloa Tete'e
- Lanu:Lanu pa'epa'e
-
O Pusa Tioata Fa'ata'ita'i Maualuga a le Matagaluega o Felauaiga a Saina, Pusa Tioata Fa'ailoga Auala mo Vali Feololo
Aoao atili- Ma'a'a o Moh:6-7
- Mamafa Fa'apitoa:2.5g/cm3
- Mafiafia o le Tele:1.5g/cm3
- Ma'a'a o Rockwell:46HRC
- Fua Fa'atatau:≥80%
- Fa'amatalaga:0.8mm-7mm, 20#-325#
- Fa'ata'ita'iga NUMERA:Mea Fa'apala'au Mata tioata
- Meafaitino:Tioata Soda Lime