Tabular Corundum Fused Alumina 99% Alumina Tabular Thermal Refractory Tabular Alumina mo le Glass Furnace Fa'atau Atoa
Aoao atili- Tulaga o le Oloa:Pauta Pa'epa'e
- Fa'amatalaga:0-1mm 1-3mm 3-5mm 5-8mm 325#
- Kalave e Vaaia:3.5g/cm3 minute
- Porosity e foliga mai:5.0% maualuga
- Fa'asusuina o le Vai:1.5% maualuga
- Al2O3:99.2 minute
- Na2O :0.40 maualuga
- Fe2O3:0.10 maualuga
- Fe2O3:0.10 maualuga
-