Pa'u lelei ua fa'afefiloi ma le pa'u alumina pa'epa'e, fa'apalapala, fa'apalapala olo
Aoao atili- Lanu:Pa'epa'e Mama
- Foliga:Kupika ma le tulimanu ma le ma'ai
- Mamafa Fa'apitoa:≥ 3.95
- Faigata o le Mohs:9.2 Mohs
- Tulaga e liusuavai ai:2150℃
- Mafiafiaga o le tele:1.50-1.95g/cm3
- Al2O3:99.4% Min
- Na2O:0.30% Maualuga
-
WA White Fused Alumina White Corundum Powder Grinding Blasting Polishing Abrasive Material
Aoao atili- Lanu:Pa'epa'e Mama
- Foliga:Kupika ma le tulimanu ma le ma'ai
- Mamafa Fa'apitoa:≥ 3.95
- Faigata o le Mohs:9.2 Mohs
- Tulaga e liusuavai ai:2150℃
- Mafiafiaga o le tele:1.50-1.95g/cm3
- Al2O3:99.4% Min
- Na2O:0.30% Maualuga
-
Pa'u Oxide Alumini Pa'epa'e WFA
Aoao atili- Lanu:Pa'epa'e Mama
- Foliga:Kupika ma le tulimanu ma le ma'ai
- Mamafa Fa'apitoa:≥ 3.95
- Faigata o le Mohs:9.2 Mohs
- Tulaga e liusuavai ai:2150℃
- Mafiafiaga o le tele:1.50-1.95g/cm3
- Al2O3:99.4% Min
- Na2O:0.30% Maualuga
-
Mea Fa'apalapala mo le oloina o le pa'u 240#-12500# Pa'u Alumina Pa'epa'e
Aoao atili- Lanu:Pa'epa'e Mama
- Foliga:Kupika ma le tulimanu ma le ma'ai
- Mamafa Fa'apitoa:≥ 3.95
- Faigata o le Mohs:9.2 Mohs
- Tulaga e liusuavai ai:2150℃
- Mafiafiaga o le tele:1.50-1.95g/cm3
- Al2O3:99.4% Min
- Na2O:0.30% Maualuga
-
Kamupani Gaosi o le White Fused Aluminum Oxide ma le Mama Maualuga
Aoao atili- AlO3:99.5%
- TiO2:0.0995%
- SiO2 (e le o se mea e leai se totogi):0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda ma Potash):0.30%
- Foliga o le Kilisitala:Vasega Rhombohedral
- Natura Fa'akemikolo:Amphoteric
- Mamafa Fa'apitoa:3.95 grm/cc
- Mafiafia o le Tele:116 pauna/ futu le maualuga
- Faigata:KNOPPS = 2000, MOHS = 9
- Tulaga e Liusuavai ai:2,000°C
-
Pa'epa'e Fused AluminA Grinding Polishing Sandblasting High Grade Refractory
Aoao atili- AlO3:99.5%
- TiO2:0.0995%
- SiO2 (e le o se mea e leai se totogi):0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda ma Potash):0.30%
- Foliga o le Kilisitala:Vasega Rhombohedral
- Natura Fa'akemikolo:Amphoteric
- Mamafa Fa'apitoa:3.95 grm/cc
- Mafiafia o le Tele:116 pauna/ futu le maualuga
- Faigata:KNOPPS = 2000, MOHS = 9
- Tulaga e Liusuavai ai:2,000°C